Numerical Analysis of Designing Antireflective Coating on the Surface of Si Optoelectric Devices

Si光电器件表面减反膜设计的数值分析

互联网摘选

The Ohmic contact and photoresponse of a ZnO single crystal film produced by MOCVD are investigated. The electrical and photoresponsive changes in the ZnO film due to the RF sputter deposition of SiO_2 ( antireflective coating) are also discussed.

对采用MOCVD方法沉积的ZnO单晶薄膜的欧姆接触特性、光电特性进行了研究，并对比研究了射频溅射沉积SiO2抗反射膜对ZnO薄膜I-V、光电特性的影响。

互联网摘选

Antireflective coating ( AR-coating) is an important optical film, which has been widely applied in the field of communication, electronics, construction, medical, biological and others.

增透膜是一种重要的光学功能薄膜，在通信、电子、建筑、医学、生物等领域具有十分广泛的应用前景。

互联网摘选

Sol-gel derived wide-band antireflective sio_2 coating used for solar heat collector

用于太阳集热器的sol-gel宽带SiO2减反膜

互联网摘选

Preparation of Silica Antireflective Coating for UV-Laser

紫外激光SiO2减反膜的制备

互联网摘选

To improve efficiency of the solar heat collector, a wide band antireflective ( AR) coating composed of nanostructure porous SiO 2 particles was designed and coated on the transparent glazing of a solar collector to reduce its reflectivity.

为了提高太阳集热器的集热效率，必须抑制透明盖板表面的反射，纳米多孔SiO2薄膜可以达到宽带减反射效果。

互联网摘选

Study on the Process of Porous Silica Antireflective Coating Solution

多孔SiO2增透膜溶液的工艺研究

互联网摘选

When getting a new prescription, make sure the lenses have an antireflective coating.

换新的眼镜时，应该确保镜片上有一层防反射膜。

互联网摘选

Study on Organosilicone Composite Antireflective Coating with High Laser Damage Threshold for Ti-Sapphire

钛宝石强激光负载的有机硅复合凝胶增透膜研究

互联网摘选

Preparation and Characterization of Hydrophobic SiO_2 Antireflective Coating

疏水性SiO2增透膜的制备与表征

互联网摘选

This antireflective coating possesses smooth and even surface, its average roughness is estimated having the value of RMS ( 1.201) and RA ( 0.934), and the specific scratch-resistant is good.

该增透膜的表面均匀性良好，均方根粗糙度（RMS）为1.201，平均粗糙度（RA）为0.934，具有一定的耐擦除性。

互联网摘选

Investigation of a-c: h films deposited on silicon solar cell as antireflective coating

α-C：H薄膜及其在硅太阳电池上作增透膜的研究

互联网摘选

Preparation of ZrO_2/ SiO_2 Antireflective Hard Coating from Sol-Gel Processing

溶胶-凝胶法制备ZrO2/SiO2双层减反硬膜

互联网摘选

With the addition of BN and boric acid, the boric acid salt glass phase formed on the surface of the samples plays the role of antireflective coating film, reduced the emissivity of the samples, and improved the absorptivity of the samples.

添加BN和硼酸后，样品表面形成的硼酸盐玻璃相充当了减反膜的角色，降低了样品的发射率，而又提高了样品的吸收率。

互联网摘选

INVESTIGATION OF A1_2O_3 ANTIREFLECTIVE COATING FOR GaAlAs HIGH SPEED LEDs The dependence of the H 2O/ TEOS molar ratio on the structure and performance of the SiO 2 antireflective coating was studied in detail.

GaAlAs快速边发光管发射端面沉积Al2O3抗反射层的研究较详细地研究了工艺参量H2O/TEOS摩尔比对薄膜结构和性能的影响。

互联网摘选

Although the porous silica antireflective ( AR) coating has high laser damage threshold after heat treatment, its transmission is correlated with environment relative humidity due to many Si-OH hydrophilic groups on the coating surface.

多孔SiO2膜层经热处理后，具有很高的激光破坏阈值，但是结构中有许多Si-OH亲水基团，导致光学透过率受环境相对湿度的影响很大。